Stanley HSP 38RC-35 OVERLAY POWDER
 |
|
Overview |
|
Specifications |
|
Email to a Friend |
|
Special gas atomized powders designed for use in all spray and fuse "puddle torches"
• Spherically shaped particles promote excellent powder flow through torch components.
• Custom balanced particle sieve distribution creates the highest powder efficiency with the lowest amount of overspray. |
|
Overview |
|
Specifications |
|
Email to a Friend |
|
STANLEY HSP 38 is a self fluxing nickel alloy powder which gives relatively soft coatings with extremely good wetting qualities. Because of its extremely low carbon content, it is often used as an underlay before putting high carbon coatings on steel.
TYPICAL PROPERTIES :
NOMINAL Fe 1.5 %, Cr 10 %, Si 3.5 %, B 2 %, C .005 %, Ni Balance
CHEMISTRY PARTICLE SIZE : -140 + 325 Mesh
Melting Temperature: 1875ºF (1020ºC)
Deposit Hardness RC 36-42
Application General repair work such as blow holes in castings, repairs to glass molds, pump parts
STANLEY HSP 38 deposits fuse to a clean oxide free surface forming a metallurgical bond with the substrate. The deposit is essentially pore-free. The fused coating can be machined using standard carbide tipped tools to a fine finish. |
|