Stanley 30 FSuper active flux coated cadmium free silver brazing alloy with 35% silver content
 |
|
Overview |
|
Specifications |
|
Email to a Friend |
|
Super active flux coated cadmium free silver brazing alloy with approximately 35% silver content
- Special "Fast Flow" flux coating provides twice the base metal cleansing action of conventional silver flux coat ings.
- No odors from rubberized compounds yet the flux coating is totally flexible and non-fragile.
- The only flux coated silver flux strong enough to clean oxidized stainless steel.
|
|
Overview |
|
Specifications |
|
Email to a Friend |
|
APPLICATIONS:
Low temperature joining of dissimilar metals. Excellent where tolerances and fit are not perfect.
FLUX COLOR: Orange
TYPICAL MECHANICAL PROPERTIES:
Undiluted Weld Metal
Tensile strength
Yield strength
Elongation
Conductivity
Density
Hardness
|
Maximum Value Up to:
64,600 PSI (441 N/mm2)
51,300 PSI (353 N/mm2)
24%
13.5
9.49/cm 3
Brinell 120 |
TORCH SETTING: Slightly carburizing
TEMPERATURE RANGES:
| Working Temperature: |
1245oF (674oC) |
| Melting Range: |
1230oF (665oC) Solidus
1440oF (755oC) Liquidus |
DEPOSITION RATES:
Diameter
(mm) |
Length
(mm) |
Weldmetal/
Rod |
Joint Length/1"
(25mm) of Rod |
| 1/16 (1.6) |
18" (450) |
.33oz (9.2g) |
24" (600mm) |
| 3/32 (2.5) |
18" (450) |
.65oz (18g) |
44" (1100mm) |
WELDING TECHNIQUES:
After cleaning metal, preheat generally to 350oF (200oC) then heat the joint area to 800oF (420oC). Melt off some flux and allow it to flow throughout the joint. Then add alloy.
ELECTRODE PACKAGING & DIMENSIONS:
| Diameter(mm) |
1/16 (1.6) |
3/32 (2.5) |
| Length (mm) |
18" (450) |
18" (450) |
| Rods / lb |
32 |
16 |
| Rods/ kg |
70 |
35 |
| Feet/lb |
48 |
24 |
| Cm/kg |
3150 |
1575 |
|
|
Overview |
|
Specifications |
|
Email to a Friend |
|
|
|
|
|
|