Stanley 816Non-synthetic , non-magnetic, high manganese stainless for joining and buffer layers
 |
|
Overview |
|
Specifications |
|
Email to a Friend |
|
Non-synthetic, non-magnetic, high manganese stainless for joining and buffer layers.
- "Non-magnetic" weld metal is not susceptible to cracking and possesses high deformation capacity.
- Joins armor steels to themselves as well as to mild, stainless and manganese steels.
- Offers a rare combination of toughness, crack resistance and impact resistance.
- Easy and complete slag removal.
|
|
Overview |
|
Specifications |
|
Email to a Friend |
|
APPLICATIONS:
For reclaiming and joining 14% manganese steels, as well as non-alloy
and alloy structural and heat treatable steels.
MICROSTRUCTURE:
Austenite with a ferrite content of 5FN.
FLUX COLOR: Grey
TYPICAL MECHANICAL PROPERTIES:
Undiluted Weld Metal
Tensile Strength
Yield Strength
Elongation
Impact Energy
Hardness
Work Hardness |
Maximum Value Up to:
101,000 PSI (690 N/mm2)
76,000 PSI (510 N/mm2)
4 0%
80J: +20oC
Brinell 200, Rockwell C25
Brinell 450, Rockwell C48 |
RECOMMENDED AMPERAGE SETTINGS:
| Diameter (mm) |
3/32 (2.5) |
1/8 (3.25) |
5/32 (4.0) |
| Minimum Amperage |
70 |
90 |
120 |
| Maximum Amperage |
90 |
120 |
150 |
WELDING POSITIONS: Flat, Horizontal, Vertical up, overhead
DEPOSITION RATES:
Diameter
(mm) |
Length
(mm) |
Weldmetal/
Electrode |
Electrodes per lb
(kg) of Weldmetal |
Arc Time of
Deposition
min/lb (kg) |
Amperage
Setting |
Recovery
Rate |
| 3/32(2.5) |
12" (300) |
.3oz (9g) |
50 (109) |
35 (76) |
80 |
110% |
| 1/8 (3.25) |
14" (350) |
.7oz (20g) |
22 (49) |
21 (46) |
105 |
110% |
| 5/32 (4.0) |
14" (350) |
1oz (29g) |
15 (33) |
18 (40) |
135 |
110% |
WELDING TECHNIQUES:
Never preheat manganese steels due to crack sensitivity. Always useminimal amperage. |
|